Personality in Science
Nanotechnologies
R&D Projects
News Of Science
Engineering
International Research & Education
Science & Technology Articles
MRC.ORG.UA

MRC ENGINEERING AND MANUFACTURING
ABOUT US PRODUCTS DESIGN PRODUCTION GALLERY VIDEO ARTICLES PARTNERS VACANCIES SITEMAP

Follow us:



MRC SCIENCE AND TECHNOLOGY
R&D PROJECTS PERSONALITY IN SCIENCE International research and education Methods of testing and research Standardization and Certification NANOTECHNOLOGY NEW ENERGY SCIENCE AND TECHNOLOGY ARTICLES


JOURNAL "DOM"
NEWS OF SCIENCE NEWS OF ENGINEERING


LINKS
Materials Research Centre Ltd. DREXEL UNIVERSITY DNI Carbon materials LINKS Yandex Search

Fracture barrier estimation by the edge fracture test method

George A. Gogotsi, Sergey P. Mudrik

Pisarenko Institute for Problems of Strength, 2 Timiryazevskaya str., 01014 Kiev, Ukraine
Received 14 July 2008; received in revised form 24 September 2008; accepted 17 October 2008 Available online 17 November 2008



CERAMICS

INTERNATIONAL



Abstract

Known methods for determining the fracture resistance of brittle materials by indentation flaking of the rectangular specimen edge are compared. The edge fracture (EF) test method was chosen as an optimum one. The investigations demonstrated that silicon carbide ceramics, submicrometre alumina, and glasses possessed fracture resistance (F R ) values that can be located above the baseline in the EF base diagram. These results emphasize that the above materials display a higher resistance to the onset of fracture (fracture barrier). This barrier can be estimated by comparing EF test data resulting from Rockwell and Vickers indentations.
© 2008 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
Keywords: C. Fracture; D. Glass; Silicon carbide; Alumina; Edge fracture; Fracture barrier


1. Introduction

The fracture behaviour of brittle materials attracts considerable attention of researchers. Different aspects of fracture behaviour are usually examined by indentation flaking (chipping) of the rectangular specimen edge. For such tests, small material quantities would be required, which is important for materials science research, especially for investigation of expensive compositions or optimization of material properties. Nowadays these investigations (see also [1] ) are performed in two different ways (A and B in Fig. 1 ). The first one employs the fracture parameter, being the distance from the point of applying the indentation load to the specimen edge. This can be performed on a special test unit with the pin-point positioning of an indenter. The second one suggests visual choice of an indentation point on the specimen surface near its edge, its further flaking on a conventional test machine, and microscopic measurement of the distance from the specimen edge to the extreme point on the chip scar ( Fig. 2 ). In all the cases, but [7] , the fracture load/adopted fracture parameter ratio is used as the general characteristic of fracture resistance, however, its calculated values do not coincide. The edge fracture (EF) test method stands out from the others, since it provides the fracture resistance characteristic proportional to fracture toughness values, determined by the single edge V-notch beam (SEVNB) method, when ceramics are consistent with the solid model of linear fracture mechanics [18] (this relation is termed the baseline [13] ). Fracture resistance values, e.g., for hot-pressed boron carbide [13] and glasses [17] , may be higher than those, obeying the above relation, which applies to other elastic dense materials. This fact was earlier overlooked, since the above first fracture stage is usually effected by preparing stress concentrators in test specimens. It is also may stem from the fact that this issue is not treated by linear fracture mechanics [18] , based on Griffith’s classical work [19] , where the propagation of an initial crack is analyzed, while its nucleation has not received mentioning [20] . Since information on this effect may be of practical interest, its investigations have been continued. The results are presented in this communication.

Flow chart of edge indentation-based fracture resistance tests for brittle materials

Fig. 1. Flow chart of edge indentation-based fracture resistance tests for brittle materials (see Refs. [ 2–5 , 8–11 , 16 ]).


Top view

Measurements of the fracture distances of glass specimens

Fig. 2. Measurements of the fracture distances L and L V on the chip scars of glass specimens (fracture load P f and L (L V ): 44 N and 0.175 mm(a), 30 Nand 0.190 mm(b)).

2. Materials and methods

Elastic oxide and nonoxide ceramics and optical quartz glass were chosen for the investigation ( Table 1 ). Their tests were carried out as described in [1] . The fracture toughness (K Ic ) was first evaluated by the SEVNB method [23] in three-point flexure of polished rectangular specimens (3-mm × 4-mm crosssection, edge radius less than 30 μm), with a V-notch of a tip radius of about 5 μm. Specimen fragments, formed in these experiments, were used in EF tests. The experiments were performed with a CeramTest device mounted on a universal test machine, with a cross-head speed being 0.5 mm/min. In SEVNB tests the loading support was used, for EF tests it was replaced by the indenter holder and X–Y table. In EF tests a Rockwell C-Scale standard conical indenter (Gilmore Diamond Tools Inc., USA) with a 200-μm tip radius and a Vickers standard pyramidal diamond indenter were impressed into visually chosen points on the rectangular specimen edge. The fracture resistance of the material was characterized by the ratio F R (F RV 1 ) of the fracture load P f to the fracture distance L (L V ) from the edge to the extreme point of the chip scar formed on the specimen surface ( Fig. 2 ), which was measured with an Olympus 51MX binocular microscope.

Table 1

Properties of examined materials.

Material K Ic (MPa m 1/2 ) F R (N/mm) F RV (N/mm) F Ra (N/mm) F' R (N/mm) Ψ Ψ V References
Optical quartz glass 0.83 ± 0.02 270 91 79 108 3.40 2.50 State Optical Institute (Russia)
Sc 2 O 3 1.49 ± 0.02 143 102 142 141 1.01 1.01 Eastern Institute of Refractory Materials (Russia) [1]
SiC EKasic ® F 2.50 ± 0.17 497 163 238 324 2.09 1.53 Wacker-Chemie GmbH (Germany) [12]
SB SiC 2.95 ± 0.02 305 146 281 273 1.09 1.12 Institute for Materials Science Problems (Ukraine) [21]
Al 2 O 3 -1 (Duralbit 90) 3.00 ± 0.06 300 154 286 281 1.05 1.07 Industrie Bitossi (Italy) [22]
Al 2 O 3 -2 (submicrometre) 3.43 ± 0.20 519 169 326 342 1.59 1.52 Fraunhofer-Institut für Keramische Technologien und Sinterwerkstoffe (Germany)
Al 2 O 3 -3 3.87 ± 0.06 340 174 371 357 0.92 0.95 Fothergill Fabrics (UK)
Si 3 N 4 4.32 ± 0.12 395 205 411 450 0.96 0.88 [13]
HP Si 3 N 4 4.29 ± 0.39 422 180 408 375 1.03 1.13 Institute for Materials Science Problems (Ukraine) [21]
HP SiC 2.45 ± 0.006 483 146 233 273 2.07 1.77 Institute for Materials Science Problems (Ukraine) [21]

3. Results and discussion

The impression of the conical indenter into the specimen surface first resulted in a Hertzian ring crack, which became the origin for a conical crack that started growing deep into the specimen. This was most evident in glass tests. But because of the edge effect, the chip scar is turned into a quasi-cone2 (Figs 3a and 4a ). The change of loading conditions resulted in the change of chip scar shapes on the specimen edges ( Fig. 3b and c ), but in Vickers indentations, quasi-cones were revealed only for quartz glass ( Fig. 3d ). Chip scars on the specimen edges of ceramics most often acquire a scallop-like shape ( Fig. 4b ).

Side view

Chip scars on glass specimen edges formed by indentations

Fig. 3. Chip scars on glass specimen edges formed after Rockwell (a) and Vickers (b) indentations, after scratching and flaking [17] (c) and on an optical quartz glass specimen after Vickers indentation (d) (P f and L: 40 N and 0.160 mm (a), 27 N and 0.230 mm (b), 17 N and 0.230 mm (c), 10 N and 0.120 mm (d)).


Side view

Chip scars on SiC

Fig. 4. Chip scars on SiC EKasic® F (a and b) and Al 2 O 3 -1 (c and d) specimen edges after Rockwell (a and c) and Vickers indentations (b and d) (P f and L (LV): 87 N and 0.170 mm (a), 15 N and 0.125 mm (b), 65 N and 0.210 mm (c), 18 N and 0.135 mm (d)).

Experimental results were analyzed using the EF base diagram with the baseline ( Fig. 5 ). As is seen, several results (data points) were located near the baseline, others fell above it, which points to the existence of the barrier to the onset of fracture for the latter. Similar results were also obtained in Ref. [6] , where the ratios of the fracture load to the distance from its application point to the specimen edge are equal to 261 N/mm at K Ic = 0.7 MPa m 1/2 and 318 N/mm at K Ic = 3.0 MPa m 1/2 for soda lime glass and RBSN, respectively. But this phenomenon was not given proper attention. Though the physical explanation of this effect is still absent, one may assume that those materials, in contrast to conventional ceramics, possess a higher resistance to the onset of fracture (crack nucleation) 3 . In Rockwell indentations, preceded by the specimen edge scratching (preformation of a stress concentrator), such a barrier was not observed, e.g., for glasses [17] . To estimate the ‘level’ of this barrier, in Refs. [13,14] additional fractographic investigation of fracture zones on the specimen edges was carried out. In this study, the ratio (damage coefficient k [13] ) of the projections of damage zone widths under the indenter to chip scar widths on the side surface of the specimen was determined. It was established that the less this ratio, the higher the barrier to the onset of fracture. The barrier to the onset of fracture can be estimated by the factor c, being the ratio of FR to its apparent value F Ra [15] (pointed lines in Fig. 5 ). For this estimation not only F R but also K Ic should be employed, since without the latter the F R location in the EF base diagram is impossible. Therefore, in both cases for determining the fracture barrier, the two methods should be used, with SEVNB requiring much larger quantities of experimental material, which is not always realizable, especially in materials science research.

Base diagram

Fig. 5. Base diagram with the baseline [14] and F RV - K Ic relation.

A knowledge of barrier levels may be of practical use in studies on ceramics for armour and cutting tools, glasses, etc., since it can become an additional source of information on the ability of the material to resist fracture. Therefore, an effort was made to simplify its estimation. It was taken into account that Vickers indentations (as well as Rockwell tests) demonstrated [1 , 12] the linear relation 4 between the fracture load P f and the fracture distance L V ( Fig. 6 ), i.e. the behaviour of brittle materials changes similarly with the fracture load.

fracture diagrams

Fig. 6. Rockwell and Vickers P f - L relations (fracture diagrams) for Al 2 O 3 -1 (a) and optical quartz glass (b).

In studies on the barrier to the onset of fracture, the specimen edges were flaked off with both indenters, and the data points were plotted in the EF base diagram ( Fig. 5 ). The data points obtained in Vickers indentations for ceramics, whose behaviour corresponds to the baseline, were approximated with the straight line, described by the equation F RV = 32K Ic + 55. It should be noted that the data points for other ceramics obtained in Vickers indentations were located in the vicinity of this line. Since in this case edge flaking started at higher stress concentrations, fracture resistance values decreased and the F RV K Ic relation, obeying the equation F R = 95K Ic + 0.5, was located at a smaller slope than the baseline in the EF base diagram. Comparative analysis of these relations, with K Ic values being excluded, gave the equation F' R = 3(F RV - 55), where F' R is the approximated fracture resistance (relationship between the above characteristics is shown by the dashed line in Fig. 5 ). Knowing F R and F' R values, one can calculate the parameter Ψ V = (F R /F' R ) (similar to Ψ [15] ), which can be used to estimate the barrier to the onset of fracture of an examined material. The Ψ and Ψ V values are summarized in Table 1 . For the materials, whose data points are located near the baseline (insignificant barrier), Ψ V is about unity (≈0.85– 1.15). But for the materials with a well-pronounced barrier, these values are much higher, e.g., for Al 2 O 3 -2, SiC EKasic® F, HP SiC, and optical quartz glass, Ψ V is 1.52, 1.53, 1.77, and 2.50. It should be noted that fracture toughness values calculated by F RV = 32K Ic + 55, using the baseline ( Fig. 5 ), are somewhat inconsistent (about 10%) with K Ic values obtained by the SEVNB method. This easily realizable and economic procedure may be considered as ‘‘qualitative’’ rather than ‘‘quantitative’’, being quite sufficient for revealing the barrier to the onset of fracture in an examined material.


4. Conclusions

The behaviour of elastic ceramics and glasses in flaking has been studied. It has been shown that the barrier to the onset of fracture of those brittle materials can be estimated by EF test results using both Rockwell and Vickers indenters. The results demonstrate the possibility of classifying brittle elastic materials by their resistance to the onset of fracture, which is quite easy to perform in a conventional laboratory, since this procedure requires simple experimental equipment and small material quantities.


References

  1. G. Gogotsi, S. Mudrik, V. Galenko, Evaluation of fracture resistance of ceramics: edge fracture tests, Ceram. Int. 33 (2007) 315–320.
  2. A. Brumm, F. Aziz, G.D. van den Bergh, M.J. Morwood, M.W. Moore, I. Kurniawan, D.R. Hobbs, R. Fullagar, Early stone technology on Flores and its implications for Homo floresiensis, Nature 441 (2006) 624–628.
  3. E.A. Almond, N.J. McCormick, Constant-geometry edge-flaking of brittle materials, Nature 321 (1986) 53–55.
  4. N.J. McCormick, E.A. Almond, Edge flaking of brittle materials, J. Hard Mater. 1 (1990) 25–51.
  5. R. Morrell, A.J. Gant, Edge chipping of hard metals, Refr. Met. Hard Met. 19 (2001) 293–301.
  6. R. Morrell, A.J. Gant, Edge chipping—what does it tell us? in: J.R. Varuer, G.D. Quinn (Eds.), Fractography of Glasses and Ceramics IV, Ceramic Transaction, American Ceramic Society, Westerville, 2001, pp. 23–41.
  7. H. Chai, B. Lawn, A universal relation for edge chipping from sharp contacts in brittle materials: a simple means of toughness evaluation, Acta Mater. 55 (2007) 2555–2561.
  8. M. Hang, R. Danzer, R. Paar, Edge toughness of brittle materials, in: G.N. Babini, M. Haviar, P. Saigalik (Eds.), Engineering Ceramics’96: Higher Reliability Through Processing, Kluwer Academic Publishers, 1997, pp. 327–335.
  9. J. Quinn, L. Su, L. Flanders, I. Lloyd, ‘‘Edge toughness’’ and material properties related to the machining of dental ceramics, Mach. Sci. Technol. 4 (2000) 291–304.
  10. J. Quinn, R. Mohan, Geometry of edge chips formed at different angles, Ceram. Eng. Sci. Proceed. 26 (2005) 85–92.
  11. J. Quinn, I. Lloyd, Flake and scratch size ratios in ceramics, in: J.R. Varuer, G.D. Quinn (Eds.), Fractography of Glasses and Ceramics IV, Ceramic Transactions, 122, American Ceramic Society, Westerville, 2001 , pp. 57–72.
  12. G. Gogotsi, S. Mudrik, A. Rendtel, Sensitivity of silicon carbide and other ceramics to edge fracture: method and results, in: E. Lara-Curzio, M. Readey (Eds.), 28th International Conference on Advanced Ceramics and Composites: A, Ceramic Engineering & Science Proceedings, Vol. 25 (3), American Ceramic Society, (2004), pp. 237–246.
  13. G.A. Gogotsi, Fracture resistance of ceramics: base diagram and R-line, Strength Mater. 38 (2006) 261–270.
  14. G.A. Gogotsi, Flaking toughness of advanced ceramics: ancient principle revived in modern times, Mater. Res. Innov. 10–2 (2006) 179–186.
  15. G.A. Gogotsi, Mechanical behaviour of a silicon nitride particular ceramic composite, Ceram. Int. 34 (2008).
  16. G.A. Gogotsi, D.Yu. Ostrovoy, B.I. Ozersky, Yu.G. Gogotsi, Methods and equipment for mechanical testing of nanostructured and other brittle materials, in: Modern Material Science: Achievements and Problems, IPMS, Kiev, 2005, pp. 907–908.
  17. G.A. Gogotsi,V.I. Galenko, S.P. Mudrik, B.I. Ozersky, V.V. Khvorostyany, T.A. Khristevich, Glass fracture in edge flaking, Strength Mater. 39 (2007) 639–645.
  18. T. Anderson, Fracture Mechanics: Fundamentals and Application, CRC Press, Bosa Raton, 1995.
  19. A.A. Griffits, The phenomena of rupture and flow in solids, Phil. Trans. Roy. Soc. Lond. A 221 (1920) 163–198.
  20. B.R. Lawn, D.B. Marshal, Mechanisms of microcontact fracture in brittle solids, in: B. Hayden (Ed.), Lithic Use-Wear Analysis, Academic press, N.Y., 1979, pp. 63–82.
  21. G.A. Gogotsi, Dr. Sci. Thesis Basic Characteristics of Mechanical Behaviour of Engineering Ceramics, IPS NASU, Kiev, 1985 (in Russian).
  22. G.A. Gogotsi, V.I. Galenko, B.I. Ozersky, T.A. Khristevich, V.I. Karban, Direct determination of fracture resistance of ceramics by the edge fracture method, Zavod. Labor. 3 (2007) 49–53.
  23. G.A. Gogotsi, Fracture toughness of ceramics and ceramic composites, Ceram. Int. 29 (2003) 777–784.
  24. G.A. Gogotsi, The problem of the classification of low-deformation materials based on the features of their behavior under load, Strength Mater. 9 (1977) 77–83.


<< ЛИЧНОСТИ НАУКИ

 

MRC ltd. / Kiev MATERIALS RESEARCH CENTRE    
www.dom.ua    

 Contact information
MRC Ltd. Materials research centre
Kiev, Krzhizhanovskogo, 3
Tel.: +38 (044) 233-24-43
Tel.: +38 (044) 237-71-87
Fax: +38 (044) 502-41-49
E-mail:
We work: Mon - Sat 10:00 - 18:00
Лицензия Creative Commons

Photos of the projects implemented by MRC TM "ДОМ", as well as articles and videos are published under the Creative Commons Attribution — with preservation of terms
(Attribution-ShareAlike) 3.0 Unported. You can freely copy, distribute, modify the materials with link to the author.

Яндекс цитирования  
name=Contacts face= 0.16